| About |
|---|
| Product Description | |
|---|---|
| Supplier | sinbo |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 300℃，10 kg | 40.99 | cm³/10min | ISO 1133 |
| Melt Flow Rate | |||
| 300℃，10 kg | 44.28 | g/10min | ASTM 1238 |
| Density | 1.08 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 10N，50mm/min | 73 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, 10N, 5mm/min | 5.3 | % | ISO 527 |
| bending strength | |||
| 3N，20mm/min | 130 | MPa | ISO 178 |
| Bending modulus | |||
| 3N，2mm/min | 4336 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| 2J ，3.8m/S | 9.60 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 141.50 | ℃ | ASTM D648 |
| 1.8 MPa | 134.99 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding process | Nominal value | Unit | Test method |
| drying temperature | 120 | ℃ | |
| Drying time | 3 | hr | |
| Suggested injection volume | 30-70 | % | |
| Melt Temperature | 290-320 | ℃ | |
| Mold temperature | 80-110 | ℃ | |
| Back pressure | 0.3-0.7 | MPa | |
| Temperature at the rear of the barrel | 265-290 | ℃ | |
| Temperature in the middle of the barrel | 275-320 | ℃ | |
| Front temperature of material barrel | 290-315 | ℃ | |
| Nozzle temperature | 295-315 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |