Formolene® 5143S

About
Formolene® 5143S is a higher melt flow homopolymer designed for light weighting of components. Its very high stiffness enables reduction of side walls and component weights without loss of top loading strength. It permits faster cycle times both in the extrusion and forming phases which can result in better process efficiencies. It is an excellent choice for ‘see-through’ house wares and rigid packaging. Formolene® 5143S has been formulated without components containing animal derivatives. Formolene® 5143S meets all requirements of the U. S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles and components of articles intended for direct food contact.&&

About

Formolene® 5143S is a higher melt flow homopolymer designed for light weighting of components. Its very high stiffness enables reduction of side walls and component weights without loss of top loading strength. It permits faster cycle times both in the extrusion and forming phases which can result in better process efficiencies. It is an excellent choice for ‘see-through’ house wares and rigid packaging. Formolene® 5143S has been formulated without components containing animal derivatives. Formolene® 5143S meets all requirements of the U. S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles and components of articles intended for direct food contact.&&

Product Description
Supplier	fpc-tw
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,Good Clarity,Quick molding cycle,Food contact compliance,Homopolymer
Availabilitys	North America
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ASTM D1505
Melt Flow Rate
230℃，2.16kg	3.0	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, injection molding	39.6	MPa	ASTM D638
Tensile strain
Yield, injection molding	7.0	%	ASTM D638
Bending modulus
1% cut, injection molding	2000	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, injection molding	37	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed, injection molded	130	℃	ASTM D648

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.