| Impact and outdoor resistant ASA with increased heat resistance for extrusion and injection moulding. (POLYMAN ASA E/MI 0515 H UV) |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | ASA |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Heat Resistance |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ISO 1183/A |
| Melt Volume Rate | |||
| 220℃，10 kg | 5.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 1.2 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 13.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 104 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 84.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A120 | 117 | ℃ | ISO 306 |
| B50 | 103 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 62631-3-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | < 100 | mm/min | ISO 3795 |
| 2.0 mm | < 100 | mm/min | FMVSS 302 |
| Flammability level | |||
| 1.5 mm | HB | ||
| 3.0 mm | HB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H 358/30 | 96.0 | MPa | ISO 2039-1 |
| Tensile modulus | 2300 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 48.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 3.0 | % | ISO 527-2/1A/50 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |