| About |
|---|
| Orgalloy® LT 4060 ES BLACK T6L resin is a black colored, very flexible polyamide alloys. Outstanding properties: easy to process, low moisture absorption, good mechanical properties at low temperature. Orgalloy® LT 4060 ES BLACK T6L resin demonstrates a good balance of properties: high flexibility (200 MPa), good thermal performance and ductility at low temperatures.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA6 Alloy |
| Material Status | Commercial: Negative |
| Features | Weather resistance is good,Excellent Processability,Ductility,Antifreeze,High Flexibility,Low moisture absorption,Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 235℃，5 kg | 0.500 | cm³/10min | ISO 1133 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 5.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.1 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 79 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 60.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 62.0 | ℃ | ISO 306 |
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | — | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 1.6 mm | HB | IEC 60695-11-10, -20 | |
| 3.2 mm | HB | IEC 60695-11-10, -20 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 50 | ISO 868 | |
| Tensile modulus | 570 | MPa | ISO 527-2 |
| tensile strength | |||
| 50% strain | 22.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |