BYNEL® Series 5000 resins are anhydride-modified polypropylene resins. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polypropylene (PP) resins. BYNEL 50E803 is a grade with a higher level of anhydride modification, and is mainly intended for use as a component in a blend with other polyolefin resins. It is not intended for extrusion in its pure form in typical extrusions or coextrusions. BYNEL 5000 series resins adhere to a variety of materials. They are most often used to adhere to PP, EVOH and polyamide. These resins are designed for applications in which EVOH or polyamide is melt coextruded with PP or PP copolymers. BYNEL 50E803 is intended mainly for blending into PP to provide PP the ability to bond to barrier resins such as polyamide or EVOH.&&

About

BYNEL® Series 5000 resins are anhydride-modified polypropylene resins. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polypropylene (PP) resins. BYNEL 50E803 is a grade with a higher level of anhydride modification, and is mainly intended for use as a component in a blend with other polyolefin resins. It is not intended for extrusion in its pure form in typical extrusions or coextrusions. BYNEL 5000 series resins adhere to a variety of materials. They are most often used to adhere to PP, EVOH and polyamide. These resins are designed for applications in which EVOH or polyamide is melt coextruded with PP or PP copolymers. BYNEL 50E803 is intended mainly for blending into PP to provide PP the ability to bond to barrier resins such as polyamide or EVOH.&&

Product Description
Supplier	DuPont
Generic	PP not specified
Material Status	Commercial: Active
Features	Good bond
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ASTM D792
Density	0.900	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	470	g/10min	ISO 1133
190℃，2.16kg	470	g/10min	ASTM D1238

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	112	℃	ASTM D1525
Vicat Softening Temp	112	℃	ISO 306
Melting peak temperature	135	℃	ASTM D3418
Melting temperature
DSC	135	℃	ISO 3146

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	160	°C
Barrel 2 zone temperature	210	°C
Barrel 3 zone temperature	235	°C
Barrel 4 zone temperature	235	°C
Barrel 5 zone temperature	235	°C
Connector temperature	235	°C
Melt temperature	< 260	°C
Nozzle temperature	235	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.