| About |
|---|
| This resin is a thixotropic, pre-accelerated, non-waxed, isophthalic unsaturated polyester resin. It shows excellent performances in fishing boats, yachts, spray-up, hand lay-up, resin transfer moulding and vacuum bagging applications. It has outstanding characteristics of non sagging and dipping. This resin has obtained the DNV Type Approval Certificate.&& |
| Product Description | |
|---|---|
| Supplier | En Chuan |
| Generic | 热固性聚酯 |
| Material Status | Commercial: Active |
| Features | Thixotropic |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| THERMAL | Nominal value | Unit | Test method |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 75.0 | ℃ | ASTM D648 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Thixotropic index | |||
| 25℃ | 2.00 to 3.00 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | |||
| 25℃ | 1.10 to 1.12 | g/cm³ | |
| viscosity | |||
| 25℃ | 0.20 to 0.70 | Pa·s | |
| Gelation time | |||
| 25℃ | 12 to 22 | min |
| Cured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 3050 | MPa | |
| — | 8830 | MPa | |
| tensile strength | |||
| — | 85.3 | MPa | |
| — | 118 | MPa | |
| Tensile strain | |||
| fracture | 2.0 | % | |
| fracture | 4.0 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Babbitt hardness | 45 | Internal Method | |
| Bending modulus | ASTM D790 | ||
| — | 6860 | MPa | ASTM D790 |
| — | 3200 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| — | 196 | MPa | ASTM D790 |
| — | 120 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Unfilled |
| 3. Filled |
| 4. Barcol 934-1 , Unfilled |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |