| Viton® AL-600 is an “AL-family” gum polymer that demonstrates improved processing when compared to its precursor Viton® B-70N. This gum provides: Higher viscosity Improved mold flow Better mold release Less mold fouling Improved compression set resistance, and Good low temperature characteristics Applications Fuel systems, such as fuel injectors O-rings Injection and transfer molding of O-rings, gaskets, and other sealing devices Extruded cords, profiles and tubing, or calendered sheets, when a blend of gum polymers are used Solution coatings of fabrics and other substrates.&& |
| Product Description | |
|---|---|
| Supplier | Chemours |
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High Viscosity,Good Dimensional Stability,Antifreeze,Good stripping performance |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.77 | g/cm³ | ASTM D792 |
| Mooney viscosity | |||
| ML 1+10，121℃ | 60 | MU | ASTM D1646 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 23 ℃ | 58 | ASTM D2240 | |
| Shore A, 23 ℃ | 72 | ASTM D2240 | |
| Shore A, 23 ℃ | 70 | ASTM D2240 | |
| Shore A, 23 ℃ | 72 | ASTM D2240 | |
| Shore A, 23 ℃ | 70 | ASTM D2240 | |
| Shore A, 23 ℃ | 74 | ASTM D2240 | |
| Shore A, 23 ℃ | 73 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| 100% strain, 23 ℃ | 4.70 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 6.80 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 6.70 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 7.60 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 6.60 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 7.70 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 7.20 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| Yield, 23 ℃ | 6.90 | MPa | ASTM D412 |
| Yield, 23 ℃ | 15.0 | MPa | ASTM D412 |
| Yield, 23 ℃ | 12.9 | MPa | ASTM D412 |
| Yield, 23 ℃ | 14.4 | MPa | ASTM D412 |
| Yield, 23 ℃ | 13.7 | MPa | ASTM D412 |
| Yield, 23 ℃ | 16.0 | MPa | ASTM D412 |
| Yield, 23 ℃ | 13.7 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| Fracture, 23 ℃ | 150 | % | ASTM D412 |
| Fracture, 23 ℃ | 230 | % | ASTM D412 |
| Fracture, 23 ℃ | 200 | % | ASTM D412 |
| Fracture, 23 ℃ | 190 | % | ASTM D412 |
| Fracture, 23 ℃ | 210 | % | ASTM D412 |
| Fracture, 23 ℃ | 200 | % | ASTM D412 |
| Fracture, 23 ℃ | 180 | % | ASTM D412 |
| tear strength | |||
| 23℃ | 23.5 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 150℃，70 hr | 9.0 | % | ASTM D395B |
| 200℃，70 hr | 14 | % | ASTM D395B |
| 200℃，168 hr | 21 | % | ASTM D395B |
| 232℃，22 hr | 11 | % | ASTM D395B |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume change | ASTM D471 | ||
| 23℃，168 hr，in M15（Fuel C/Methanol 85/15） | 33 | % | ASTM D471 |
| 200 ℃, 70 hr, in IRM 903 oil | 2.5 | % | ASTM D471 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min, Aged in M15 (Fuel C/Methanol 85/15) for 168 hr at 73°F |
| 3. 20 in/min, Aged for 70 hr at 392°F |
| 4. 20 in/min, Aged in IRM 903 Oil for 70 hr at 392°F |
| 5. 20 in/min, Aged for 168 hr at 392°F |
| 6. 20 in/min, Aged for 24 hr at 450°F |
| 7. 20 in/min, Aged for 70 hr at 482°F |
| 8. 20 in/min, Aged for 168 hr at 482°F |
| 9. Die C |
| 10. Aged in M15 (Fuel C/Methanol 85/15) for 168 hr at 73°F |
| 11. Aged for 70 hr at 392°F |
| 12. Aged in IRM 903 Oil for 70 hr at 392°F |
| 13. Aged for 168 hr at 392°F |
| 14. Aged for 24 hr at 450°F |
| 15. Aged for 70 hr at 482°F |
| 16. Aged for 168 hr at 482°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |