| Microthene F polyolefin powders are ultra-fine, sperically shaped particles with narrow size distribution suitable for use in a broad range of specialty applications. Microthene F powders combine the unique properties of a polyolefin resin with a microfine particle size. Materials may contain flow-enhancing agents as required for processing and handling.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Copolymer |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 8.0 | g/10min | ASTM D1238 |
| Average particle size | 20 | µm | ETM Malvern |
| Particle Shape | Spherical | ||
| Particle size distribution | 5.0 to 50.0 | µm | ETM Malvern |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 38 | ASTM D2240 | |
| tensile strength | |||
| fracture | 11.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 680 | % | ASTM D638 |
| Bending modulus | 93.1 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 75.0 | ℃ | ASTM D1525 |
| Melting peak temperature | 96.0 | ℃ | ASTM D3418 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Maximum Moisture Content | 0.10 | % | ETM 156 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |