COSMOPLENE® AZ564

About
COSMOPLENE AZ564 is high impact PP copolymer manufactured by gas phase process licensed from Sumitomo Chemical Co. Japan. COSMOPLENE AZ564 is high flow, high stiffness, high impact copolymer grade which can perform faster injection cycle and thinner gauge. COSMOPLENE AZ564 is specially designed for large item, wide area, thin gauge, low stress products such as tub and lid of washing machine, thin wall containers, TV back cover, automotive door trims etc.&&

About

COSMOPLENE AZ564 is high impact PP copolymer manufactured by gas phase process licensed from Sumitomo Chemical Co. Japan. COSMOPLENE AZ564 is high flow, high stiffness, high impact copolymer grade which can perform faster injection cycle and thinner gauge. COSMOPLENE AZ564 is specially designed for large item, wide area, thin gauge, low stress products such as tub and lid of washing machine, thin wall containers, TV back cover, automotive door trims etc.&&

Product Description
Supplier	TPC
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,High liquidity,Impact copolymer,HB
Availabilitys	Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ASTM D792
Melt Flow Rate	30	g/10min	ASTM D1238
Shrinkage rate			Internal Method
MD：2.0 mm	1.5	%	Internal Method
TD：2.0 mm	1.5	%	Internal Method

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ASTM D256
-20℃	40	J/m	ASTM D256
23℃	71	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	121	℃	ASTM D648

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	90		ASTM D785
tensile strength			ASTM D638
yield	26.5	MPa	ASTM D638
fracture	19.0	MPa	ASTM D638
Tensile strain
fracture	150	%	ASTM D638
Bending modulus	1180	MPa	ASTM D790

Process Conditions
injection	Nominal value	Unit	Test method
Barrel rear temperature	190 to 230	°C
Barrel middle temperature	190 to 230	°C
Barrel front temperature	190 to 230	°C
Mold temperature	30	°C
Injection pressure	6.86	MPa
Clamping force	0.98	kN/cm²

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.