| About |
|---|
| 400F (205C) HDT. 3.3 Notched Izod. Excellent chemical resistance&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Active |
| Features | Solvent resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.3 to 1.7 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.54 | % | |
| Equilibrium, 23 ℃ | 4.4 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 66.0 | MPa | |
| fracture | 59.0 | MPa | |
| Tensile strain | |||
| yield | 9.0 | % | |
| fracture | 50 | % | |
| Bending modulus | |||
| 100 mm span | 2370 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 99.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 110 | J/m | |
| 23℃ | 180 | J/m | |
| Dart impact equipped with measuring instruments | |||
| -30℃，Energy at Peak | 24.0 | J | |
| 23℃，Energy at Peak | 40.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 204 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 125 | ℃ | |
| Vicat Softening Temp | 245 | ℃ | ASTM D1525 4 |
| Linear coefficient of thermal expansion | |||
| MD：-20~150℃ | 9.5E-5 | 1/℃ | |
| TD：-20：150℃ | 8.1E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.7E+16 | ohms | ASTM D257 |
| Volume resistivity | 4.4E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in oil | 26 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 60 Hz | 3.27 | ||
| 50 kHz | 3.27 | ||
| 1 MHz | 2.76 | ||
| Dissipation factor | |||
| 50 Hz | 0.039 | ||
| 60 Hz | 0.039 | ||
| 1 MHz | 0.019 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95 to 105 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Recommended injection volume | 30 to 50 | % | |
| Barrel rear temperature | 255 to 295 | °C | |
| Barrel middle temperature | 260 to 295 | °C | |
| Barrel front temperature | 265 to 295 | °C | |
| Nozzle temperature | 270 to 295 | °C | |
| Processing (melt) temperature | 270 to 295 | °C | |
| Mold temperature | 65 to 95 | °C | |
| Back pressure | 0.300 to 1.40 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.013 to 0.038 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |