ForTii® Eco E61 (P836B)

About
30% Glass Reinforced, High Flow, for E&E applications Special Features: Contains release agent Good or high flow Lubricated Used In: Audio Jack Connectors ForTii® is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries. We developed ForTii® in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €” and need. That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.

About

30% Glass Reinforced, High Flow, for E&E applications Special Features: Contains release agent Good or high flow Lubricated Used In: Audio Jack Connectors ForTii® is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries. We developed ForTii® in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €” and need. That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.

Product Description
Supplier	DSM
Generic	PA 4T
Material Status	Commercial: Active
Features	Good liquidity,Lubricating
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.39	g/cm³
Shrinkage rate
TD	1.2	%
MD	0.35	%

MECHANICAL	Nominal value	Unit
Tensile modulus	11000	MPa
tensile strength
fracture	190	MPa
Tensile strain
fracture	2.3	%
Bending modulus	9700	MPa
bending strength	280	MPa

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	10	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
1.8 MPa, unannealed	265	℃
Glass transition temperature	100	℃
Melting temperature	325	℃
Linear coefficient of thermal expansion
MD	2.0E-5	1/℃
TD	7.0E-5	1/℃

Electrical performance	Nominal value	Unit	Test method
Relative permittivity
1.00 GHz	3.70
10.0 GHz	3.60

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flammability level
0.8 mm	HB
1.5 mm	HB

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	100	°C
Drying time	2.0	hr
Barrel rear temperature	310 to 320	°C
Barrel middle temperature	315 to 325	°C
Barrel front temperature	320 to 325	°C
Nozzle temperature	320 to 325	°C
Processing (melt) temperature	320 to 330	°C
Mold temperature	80 to 150	°C
Injection speed	中等偏快
Back pressure	0.500 to 3.00	MPa
Screw compression ratio	2.5:1.0

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.