| About |
|---|
| Clyrell EC348P is a clarified and antistatic formulated polyolefin designed for injection molding applications that combines the typical advantages of polypropylene random and impact copolymers. Clyrell EC348P features excellent transparency, very high gloss combined with a good stiffness/impact strength balance. Customers typically use Clyrell EC348P to produce clear, shock-resistant food and non-food containers and houseware articles.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good surface appearance,High impact resistance,noise reduction,Nucleation,Antistatic property |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 16 | g/10min | ASTM D1238 |
| 230℃，2.16kg | 14 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 19.0 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 1.0 | kJ/m² | ISO 179/1eA |
| 0℃ | 2.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 67.2 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 75.0 | ℃ | ISO 75-2/B |
| Toughness/brittle transition temperature | -5.00 | ℃ | ISO 6603-2 |
| Vicat Softening Temp | |||
| A50 | 128 | ℃ | ISO 306/A50 |
| B50 | 65.0 | ℃ | ISO 306 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 1000 µm | 13 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 46.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1200 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 28.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 13 | % | ISO 527-2 |
| fracture | > 50 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |