| Polypropylene homopolymer compound filled with 40% aethetic rigid talc. Flowability specifc for injection molding of aethetic particulars; high rigidity and dimensional planarity at hight temperatures. Available in natural version and colored as per sample.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,Good Dimensional Stability,Good liquidity,Homopolymer,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.90 | % | ISO 294-4 |
| MD | 0.90 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.020 | % | ISO 62 |
| Ash Content | 40 | % | ISO 3451 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 18 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | 2.1 | kJ/m² | ISO 180-1A |
| 23℃ | 2.5 | kJ/m² | ISO 180-1A |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Accelerate oven aging | |||
| 150℃ | 6.3 | day | ISO 4577 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 131 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 154 | ℃ | ISO 306/A50 |
| B50 | 100 | ℃ | ISO 306 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 335 | |
| Linear coefficient of thermal expansion | |||
| MD | 6.0E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 78 | ISO 868 | |
| tensile strength | ISO 527-2/20 | ||
| Yield, 23 ℃ | 30.0 | MPa | ISO 527-2/20 |
| Fracture, 23 ℃ | 28.0 | MPa | ISO 527-2/20 |
| Tensile strain | ISO 527-2/20 | ||
| Yield, 23 ℃ | 3.0 | % | ISO 527-2/20 |
| Fracture, 23 ℃ | 5.0 | % | ISO 527-2/20 |
| Bending modulus | |||
| 23℃ | 4400 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 48.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 200 to 240 | °C | |
| Mold temperature | 50 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50%RH |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |