Designed to address the problems associated with impact loads, NYCAST 6MP formulations provide performance advantages in applications that require improved impact properties over standard grades. NYCAST 6MP cushion pads protect the hammer from metal-to-metal damage in pile drivers and provide many performance advantages in certain gear, die block, valve seat and other applications. This formulation also provides superior performance in extreme cold temperature applications, where standard grades are prone to impact failure. High impact resistance High tensile elongation Resistance to brittleness and deterioration Can work under low temperature circumstances Noise dampening&&

About

Designed to address the problems associated with impact loads, NYCAST 6MP formulations provide performance advantages in applications that require improved impact properties over standard grades. NYCAST 6MP cushion pads protect the hammer from metal-to-metal damage in pile drivers and provide many performance advantages in certain gear, die block, valve seat and other applications. This formulation also provides superior performance in extreme cold temperature applications, where standard grades are prone to impact failure. High impact resistance High tensile elongation Resistance to brittleness and deterioration Can work under low temperature circumstances Noise dampening&&

Product Description
Generic	PA6
Material Status	Commercial: Active
Features	High impact resistance,Antifreeze
Availabilitys	North America
Process Methods	casting

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.14 to 1.16	g/cm³	ASTM D792
Water absorption rate			ASTM D570
24hr	0.50 to 0.60	%	ASTM D570
saturated	5.0 to 6.0	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	44 to 49	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	204 to 221	℃	ASTM D648
1.8 MPa, unannealed	93.3 to 204	℃	ASTM D648
Continuous use temperature	110	℃	ASTM D794
Melting temperature	227 to 238	℃
Linear coefficient of thermal expansion
MD	7.2E-5 to 8.1E-5	1/℃	ASTM D696
Operating temperature
Intermittent	166	℃

Electrical performance	Nominal value	Unit	Test method
Dielectric strength	20 to 24	kV/mm	ASTM D149
Dielectric constant			ASTM D150
60 Hz	3.70		ASTM D150
1 kHz	3.70		ASTM D150
100 kHz	3.70		ASTM D150

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	76 to 78		ASTM D2240
Rockwell hardness
R-level	110 to 115		ASTM D785
Tensile modulus	2590 to 3030	MPa	ASTM D638
tensile strength	66.9 to 74.5	MPa	ASTM D638
Tensile strain
fracture	25 to 35	%	ASTM D638
Bending modulus	2280 to 2410	MPa	ASTM D790
bending strength	82.7 to 89.6	MPa	ASTM D790
Compression modulus	1930 to 2380	MPa	ASTM D695
compressive strength	86.2 to 104	MPa	ASTM D695
shear strength	68.9 to 75.8	MPa	ASTM D732
friction coefficient
With oneself – dynamic	0.22		ASTM D1894
Load deformation	1.00 to 2.00	%	ASTM D621

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.