| FRAGOM is the trade-mark of our flame retardant halogen free polyolefine compounds. FRAGOM G/991 XA flame retardant crosslinkable compound having GOOD RESISTANCE TO OIL for insulation and sheathing. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 SCU. To use in solar cables sheathing (TUV) we suggest to add 10-11 % of catalyst MAC/500 REACTION BETWEEN GRAFTING AND CATALYST These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 CERTIFY VDE 0207-24 HM3, BS 7655 EI5, CEI 2011 M2-EM2, IEC 60092-359 SHF2&& |
| Product Description | |
|---|---|
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Crosslinked,Halogen free,Flame Characteristics,Grease resistance,Fuel resistance |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 7.0 to 12 | g/10min | ASTM D1238 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | IEC 60811 | ||
| 127℃，40 hr | 15 | % | IEC 60811 |
| 135℃，168 hr | 20 | % | IEC 60811 |
| Changes in tensile stress during fracture in air | IEC 60811 | ||
| 127℃，40 hr | -7.0 | % | IEC 60811 |
| 135℃，168 hr | -10 | % | IEC 60811 |
| The rate of change in tensile strength | IEC 60811 | ||
| 70℃，168 hr | -10 | % | IEC 60811 |
| 100℃，168 hr | -20 | % | IEC 60811 |
| Change rate of ultimate elongation | IEC 60811 | ||
| 70℃，168 hr | -15 | % | IEC 60811 |
| 100℃，168 hr | -19 | % | IEC 60811 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | IEC 60811 | ||
| 250℃ | 70 | % | IEC 60811 |
| Residual：250℃ | 5.0 | % | IEC 60811 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Conductivity | < 10.0 | µS/mm | IEC 60754-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 32 | % | ASTM D2863 |
| Halogen Content | < 0.300 | % | IEC 60754-1 |
| toxicity | |||
| pH | > 4.30 | IEC 60754-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 45 | ASTM D2240 | |
| tensile strength | > 13.0 | MPa | IEC 60811 |
| Tensile strain | |||
| fracture | > 250 | % | IEC 60811 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 150 | °C | |
| Barrel 2 zone temperature | 170 | °C | |
| Barrel 3 zone temperature | 180 | °C | |
| Barrel 4 zone temperature | 195 | °C | |
| Head temperature | 205 | °C | |
| Nozzle temperature | 215 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 N/cm² |
| 3. Air Bomb |
| 4. Heat Aging |
| 5. Aging in IRM 903 oil |
| 6. Aging in IRM 902 oil |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |