| About |
|---|
| PA66 blend with partially aromatic content, 40% glass fibre reinforced, heat stabilization as well as reduced density. For all kind of injection moulding parts with high requirements to stiffness with a density advantage.&& |
| Product Description | |
|---|---|
| Supplier | TER |
| Generic | PA 66+PA 6I/6T |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Aromatic,Heat Stabilized |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 3.8 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.4 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11500 | MPa | |
| tensile strength | |||
| fracture | 175 | MPa | |
| Tensile strain | |||
| fracture | 3.0 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 80 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 225 | ℃ | |
| 1.8 MPa, unannealed | 210 | ℃ | |
| Melting temperature | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 33 | kV/mm | |
| Compared to the leakage tracing index | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |