| About |
|---|
| Daplen EF103AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection moulding. This material has excellent balanced mechanical properties, high melt flow rate and gives a good surface quality. Applications Daplen EF103AE has been developed especially for the car industry to be used in automotive exterior parts. Bumpers Body side mouldings Body panels Special features Suitable for applications, which require low expansion over a broad temperature scale High flowability allowing to mould complex-structured parts with very high “flow path / wall thickness ratios”&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High liquidity |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.970 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 16 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| — | 0.85 | % | |
| 90℃，2 hrs | 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 18.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 8.0 | % | |
| fracture | > 100 | % | |
| Bending modulus | 1200 | MPa | ISO 178 |
| bending strength | 22.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 5.4 | kJ/m² | ISO 179/1eA |
| -20℃ | 6.6 | kJ/m² | ISO 179/1A |
| 23℃ | 46 | kJ/m² | ISO 179/1A |
| Charpy Unnotch Impact strength | ISO 179/1U | ||
| -20℃ | 210 | kJ/m² | |
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | 6.5 | kJ/m² | |
| 23℃ | 44 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 83.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 48.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 40.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 8.0E-5 | 1/℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 | °C | |
| Drying time | 2.0 | hr | |
| Hopper temperature | 40.0 to 80.0 | °C | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 30.0 to 50.0 | °C | |
| Hold pressure | 30.0 to 60.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. disk |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |