| About |
|---|
| P6006NA is a high density Polyethylene (potentially ASTM PE4710 cell class requirements) with multimodal distribution of the molecular mass. This is natural color grade suitable for pipe extrusion with excellent combination of properties. It is also suitable for use in telecommunication ducting, corrugated pipes and spiral pipes. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 6.2 | g/10min | |
| 190℃，5.0kg | 0.23 | g/10min | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 25 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 74.0 | ℃ | ISO 306/B |
| Oxygen induction time (210 ° C) | > 20 | min | EN 728 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 63 | ASTM D2240 | |
| Tensile modulus | 850 | MPa | ASTM D638 |
| Tensile strength (yield, molded) | 23.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2 |
| Bending creep modulus | 1.05 | GPa | DIN 19537-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |