| About |
|---|
| HANWHA EVA 2030 is manufactured by DOW tubular high pressure process and designed for variety of film application such as multiplayer agricultural film. EVA 2030 has well balanced property of high clarity, mechanical property and processability.&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Smoothness,High anti-blocking,Inoxidizability |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.927 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| Vinyl acetate content | 6.5 | wt% | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 60 | µm | |
| tensile strength | ASTM D882 | ||
| fracture | 18.6 | MPa | ASTM D638 |
| MD, fracture, 60 µ m | 25.5 | MPa | ASTM D882 |
| TD, fracture, 60 µ m | 23.5 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| fracture | 740 | % | ASTM D638 |
| MD, fracture, 60 µ m | 350 | % | ASTM D882 |
| TD, fracture, 60 µ m | 650 | % | ASTM D882 |
| Drop hammer impact | |||
| 60 µm | > 400 | g | ASTM D1709 |
| tear strength | ASTM D1004 | ||
| MD，60 µm | 83.4 | kN/m | ASTM D1004 |
| TD，60 µm | 88.3 | kN/m | ASTM D1004 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 83.0 | ℃ | ASTM D1525 |
| Melting peak temperature | 101 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 60 µm | 4.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 140 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |