| Celazole TU-60 is a high performance unfilled blend, ideal for applications requiring no fillers. This material works well for complex geometries and offers the best process ability. Ideal for lamp sockets, connectors and back up seals.&& |
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Excellent Processability,Solvent resistance |
| Availabilitys | North America |
| Process Methods | Extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | |
| Water Absorption | |||
| balance | 6.5 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Coeff. of linear thermal expansion | |||
| MD | TMA | ||
| 24 to 149 ℃ | 3.4E-5 | cm/cm/℃ | TMA |
| 199 to 299 ℃ | 7.0E-5 | cm/cm/℃ | TMA |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 2.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.40 | ASTM D150 | |
| 10 kHz | 3.40 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.0 | ASTM D150 | |
| 10 kHz | 1.0E-3 | ASTM D150 | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Supplementary Information | Nominal value | Unit | Test method |
|---|---|---|---|
| Initial weight loss temperature | Internal Method | ||
| Air | 499 | ℃ | Internal Method |
| nitrogen | 499 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| A-level | 25 | ASTM D785 | |
| Tensile Modulus | 5030 | MPa | ASTM D638 |
| Tensile Strength | 100 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK | 2.2 | % | ASTM D638 |
| Flexural Modulus | 5000 | MPa | ASTM D790 |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Compression Modulus | 2960 | MPa | ASTM D695 |
| Compressive Strength | 207 | MPa | ASTM D695 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |