| Kingfa ABP-1012是一种聚丙烯材料,含有的填充物为10% 填料。 该产品在北美洲或亚太地区有供货,。 Kingfa ABP-1012的主要特性有: 阻燃/额定火焰 附着力强 Kingfa ABP-1012的典型应用领域为:汽车行业&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Sprayable,Good bond,HB |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.970 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：23℃ | 1.1 to 1.3 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30 ℃, 3.2mm, injection molding | 70 | J/m | ASTM D256 |
| 23 ℃, 3.2mm, injection molding | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm, injection molded | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm, injection molded | 47.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 65 | ASTM D785 | |
| tensile strength | |||
| 23 ℃, injection molding | 17.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, injection molding | 200 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, injection molding | 1060 | MPa | ASTM D790 |
| bending strength | |||
| 23 ℃, injection molding | 25.0 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |