| Optix® CP-927HF是一种聚甲基丙烯酸甲酯-丙烯酸材料,。 该产品在北美洲或欧洲有供货,加工方式为:注射成型。 Optix® CP-927HF的主要特性有: 阻燃/额定火焰 无气味/无味道 高流动性 加工性能良好 绝缘&& |
| Product Description | |
|---|---|
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good Clarity,High impact resistance,Good Dimensional Stability,High liquidity,Machinable,Low odor,Solvent resistance,Insulation,HB |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 11 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 53 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 670 | J/m | ASTM D256 |
| Drop hammer impact | 2.82 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 77.8 | ℃ | ASTM D648 |
| Vicat Softening Temp | 93.3 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 7.5E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.490 | ASTM D542 | |
| Transmittance | 91.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ASTM D638 |
| tensile strength | 50.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 18 | % | ASTM D638 |
| Bending modulus | 2140 | MPa | ASTM D790 |
| bending strength | 75.8 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 53 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 66 to 74 | °C | |
| Barrel rear temperature | 204 to 249 | °C | |
| Barrel middle temperature | 210 to 254 | °C | |
| Barrel front temperature | 216 to 260 | °C | |
| Nozzle temperature | 210 to 260 | °C | |
| Processing (melt) temperature | 210 to 249 | °C | |
| Mold temperature | 49 to 79 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |