| About |
|---|
| Specialty Filled PC/Polyester Alloy&& |
| Product Description | |
|---|---|
| Supplier | EnCom |
| Generic | PC + Polyester |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 to 0.50 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 105 | MPa | ASTM D638 |
| Bending modulus | 6360 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 85 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 171 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 88 to 110 | °C | |
| Drying time | 2.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 243 to 271 | °C | |
| Barrel middle temperature | 249 to 277 | °C | |
| Barrel front temperature | 257 to 282 | °C | |
| Nozzle temperature | 254 to 274 | °C | |
| Processing (melt) temperature | 260 to 279 | °C | |
| Mold temperature | 18 to 66 | °C | |
| Back pressure | 0.172 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |