| TITANZEX® HB5200 is a High Density Polyethylene material. It is available in Asia Pacific for blow molding. Important attributes of TITANZEX® HB5200 are: Good Stiffness High ESCR (Stress Crack Resistant) Impact Resistant Typical applications include: Containers Consumer Goods&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,High ESCR |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.20 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | 250 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 128 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 63 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 25.5 | MPa | ASTM D638 |
| fracture | 32.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 500 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 981 | MPa | ASTM D747 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |