| Menzolit® SMC 1100 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn’t melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor heavy metals. Menzolit® SMC 1100 is a special vinylester SMC for high strength applications. The reinforcement has been put to a level that combines mouldability with high strength and stiffness properties. The specific resin and a higher amount of glass fibers results in high mechanical strength. Durability is improved as well. Even without a specific fire retardant, the fire retardancy level HB according UL 94 is achieved. Typical applictions are structural components within the automotive industry or mechanical engineering. It is suitable for load carrying applications or fast moving and accelerated components.&& |
| Product Description | |
|---|---|
| Generic | 热固性聚酯 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Low smoke,Halogen free,Flame Characteristics,High Heat Resistance,HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.80 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| — | 0.040 | % | ISO 2577 |
| — | 0.0 | % | DIN 53464 |
| Water absorption rate | |||
| Saturation, 23 ℃ | < 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| Compression Molding | 13000 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, molding | 150 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | 1.6 | % | ISO 527-2 |
| Bending modulus | |||
| Compression Molding | 13000 | MPa | ISO 178 |
| bending strength | |||
| Compression Molding | 280 | MPa | ISO 178 |
| compressive strength | 120 | MPa | ISO 14126 |
| Poisson’s ratio | 0.30 | Internal Method | |
| Matrix Crazing Strain | 0.60 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| Compression Molding | 130 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 200 | ℃ | ISO 75-2/A |
| Continuous use temperature | 170 | ℃ | Internal Method |
| Glass transition temperature | 162 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | 1.2E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Mold temperature | 135 to 160 | °C | |
| Injection pressure | 8.00 to 10.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Post Molding Shrinkage |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |