| About |
|---|
| LNP Thermocomp compound DX14354X is an improved flow, colorable compound based on PC copolymer resin developed for applications that require Laser Direct Structuring (LDS) for antenna, or electronic circuit manufacturing. Thermocomp compound DX14354X helps customers to improve productivity with stable plating and RF performance, excellent impact strength and surface finish.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Copolymer,Good coloring |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：24 hrs | 0.50 | % | ASTM D995 |
| TD：24 hrs | 0.70 | % | ASTM D995 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 54 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 5 | % | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 2500 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 85 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2500 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 111 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.2E+16 | Ω.cm | ASTM D257 |
| Surface resistance | 1.2E+16 | Ω.cm | ASTM D257 |
| Dielectric constant | |||
| 3.10 | 1 GHz | ASTM D150 | |
| Dissipation factor | |||
| 6.0E-3 | 1 GHz | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.0mm | V-1 | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 750 | J/m | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 -120 | °C | |
| Drying time | 2-4 | Hr | |
| Water content | 0.02 | % | |
| Injection temperature | |||
| Rear barrel temperature | 230-245 | °C | |
| Central temperature of the barrel | 240-255 | °C | |
| Barrel front temperature | 245-265 | °C | |
| Mold temperature | 40-100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. After 40 cycles, Similar to USCAR-2, Class IV |
| 5. After 40 cycles, Similar to USCAR-2, Class III |
| 6. 0.051 in/min |
| 7. 0.079 in/min |
| 8. at Yield |
| 9. 80*10*3 mm |
| 10. 80*10*4 mm |
| 11. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |