Hifax CA 1133 A

About
Hifax CA 1133 A, is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’s proprietary Catalloy process technology. It is used for injection molding. Hifax CA1133 A is in particular suitable for high impact strength applications, even at low temperature. The product is characterised both by medium rigidity and a very good processability as well as and excellent paintability. The grade is available in natural pellet form. For regulatory compliance information see Hifax CA 1133 A Regulatory Affairs Product Stewardship Information/Certification Data Sheet (RAPIDS), which can be found on www.polymers.lyondellbasell.com.&&

About

Hifax CA 1133 A, is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’s proprietary Catalloy process technology. It is used for injection molding. Hifax CA1133 A is in particular suitable for high impact strength applications, even at low temperature. The product is characterised both by medium rigidity and a very good processability as well as and excellent paintability. The grade is available in natural pellet form. For regulatory compliance information see Hifax CA 1133 A Regulatory Affairs Product Stewardship Information/Certification Data Sheet (RAPIDS), which can be found on www.polymers.lyondellbasell.com.&&

Product Description
Supplier	LyondellBasell
Generic	Polyolefin Elastomer
Material Status	Commercial: Active
Features	Excellent Processability,High impact resistance,Sprayable,low-temperature impact resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.890	g/cm³	ISO 1183/A
Melt Flow Rate
230℃，5.0kg	16	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	54		ISO 868
tensile strength
yield	17.0	MPa	ISO 527-2
Tensile strain
fracture	> 200	%	ISO 527-2
Bending modulus	850	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/1A
-40℃	7.0	kJ/m²	ISO 180-1A
-20℃	9.0	kJ/m²	ISO 180-1A
23℃	No Break		ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	60.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	122	℃	ISO 306/A50

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.