| LAPEROS® S478是一种液晶聚合物（LCP）产品,含有的填充物为40% 玻璃矿物。 它,在亚太地区有供货。 特性包括: 阻燃/额定火焰 高刚度 高流动性 抗翘曲 耐热 |
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,High liquidity,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.72 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：1 mm | 0.39 | % | |
| TD：1 mm | 0.080 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strength | 100 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.8 | % | ASTM D638 |
| Bending modulus | 10000 | MPa | ISO 178 |
| Bending stress | 135 | MPa | ISO 178 |
| Bending strain | 2.2 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 290 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 38 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 kHz | 4.40 | ||
| 1 MHz | 4.00 | ||
| Dissipation factor | |||
| 1 kHz | 0.020 | ||
| 1 MHz | 0.020 | ||
| Arc resistance | 183 | sec | ASTM D495 |
| Compared to the leakage tracing index | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |