| About |
|---|
| Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Internal mold release. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant and also halogen free according VDE/DIN 472 part 815.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 16 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 360℃，5 kg | 8.50 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD | 0.50 to 0.70 | % | |
| MD：3.2 mm | 0.50 to 0.70 | % | |
| TD：3.2 mm | 0.50 to 0.70 | % | |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 1.8 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.65 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -30℃ | 74 | J/m | ASTM D256 |
| 23℃ | 69 | J/m | ASTM D256 |
| -30℃ | 5.9 | kJ/m² | ISO 180-1A |
| 23℃ | 6.2 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ASTM D4812 | |
| -30℃ | 150 | kJ/m² | ISO 180/1U |
| 23℃ | 200 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 33.9 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 237 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 217 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 230 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 228 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 242 | ℃ | ASTM D1525, ISO 306/B50 12 18 |
| B120 | 240 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~150℃ | 5.0E-5 | 1/℃ | ASTM E831 |
| MD：23~150℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~150℃ | 5.0E-5 | 1/℃ | ASTM E831 |
| TD：23~150℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.22 | W/m/K | ASTM E1530 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 3.2 mm in oil | 14 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 100 Hz | 3.38 | ||
| 1 kHz | 3.37 | ||
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 0.018 | ||
| 60 Hz | 0.018 | ||
| 100 Hz | 8.0E-3 | ||
| 1 kHz | 1.0E-3 | ||
| 1 MHz | 7.0E-3 | ||
| Compared to the leakage tracing index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 3.2 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 3 mm | 850 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 45 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 138 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 3520 | MPa | ASTM D638 |
| — | 3130 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 96.5 | MPa | ASTM D638 |
| yield | 95.0 | MPa | ISO 527-2/5 |
| fracture | 96.5 | MPa | ASTM D638 |
| fracture | 78.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 8.4 | % | ISO 527-2/5 |
| fracture | 50 | % | ASTM D638 |
| fracture | 50 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 3170 | MPa | ASTM D790 |
| — | 3080 | MPa | ISO 178 |
| bending strength | |||
| — | 123 | MPa | ISO 178 |
| Yield, 100 mm span | 155 | MPa | ASTM D790 |
| Fracture, 50 mm span | 158 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.20 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. at Break |
| 8. 0.10 in/min |
| 9. 80*10*4 sp=62mm |
| 10. 80*10*4 mm |
| 11. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |