| High impact modified PP copolymer recycling compound. The product can contain up to 3,5% mineral substances – Black colored.&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | High impact resistance,Copolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ISO 1183/A |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 10.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 1.3 to 2.0 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 2.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 21 | kJ/m² | |
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 137 | ℃ | ISO 306/A50 |
| B50 | 64.0 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | < 100 | mm/min | ISO 3795 |
| Flammability level | |||
| 1.5 mm | HB | ||
| 3.0 mm | HB |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H 132/30 | 54.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1100 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 24.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 11 | % | ISO 527-2/1A/50 |
| Bending modulus | 1100 | MPa | ISO 178 |
| bending strength | 29.0 | MPa | ISO 178 |
| Bending strain | 7.0 | % | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |