| About |
|---|
| TF-Y822-BP (750 ppm Slip, 3150 ppm Antiblock): Industrial packaging, high strength liners TF-Y822-CP (6000 ppm Antiblock): Heavy duty sacks, high strength packaging&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Smoothness,High anti-blocking,Machinable,Food contact compliance,Low density,Hexene copolymers |
| Availabilitys | North America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.921 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | |||
| 1% secant, TD, 25 µ m, blow molded film | 280 | MPa | ASTM D882 |
| 1% secant, MD, 25 µ m, blow molded film | 230 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 25 µ m, blow molded film | 42.0 | MPa | ASTM D882 |
| TD, yield, 25 µ m, blow molded film | 12.0 | MPa | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 49.0 | MPa | ASTM D882 |
| MD, yield, 25 µ m, blow molded film | 12.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 25 µ m, blow molded film | 810 | % | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 560 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 130 | g | ASTM D1709-A |
| tear strength | |||
| TD, 25 µ m, blow molded film | 540 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 350 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 53 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 13 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Low friction puncture | |||
| Blow molded film, 25.0 µ m | 430 | J/cm | Internal Method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |