| About |
|---|
| NORYL PX1181 PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is an unfilled , injection moldable grade, with improved impact performances, an ISO 306 Vicat B/120 temperature of 120 deg C and a UL94 HB rating . This grade has been developed for automotive interior applications requiring standard ECE dashboard impact test. NORYL PX1181 is an opaque material available in limited colors only.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，5 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.14 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 25 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 11 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 115 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 105 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| A50 | 130 | ℃ | ISO 306/A50 |
| B50 | 115 | ℃ | ISO 306 |
| B120 | 120 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 73~77℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 7.0E-5 | 1/℃ | |
| TD：23~80℃ | 9.0E-5 | 1/℃ | |
| Thermal conductivity coefficient | 0.22 | W/m/K | ISO 8302 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 50 Hz | 2.70 | ||
| 60 Hz | 2.70 | ||
| 1 MHz | 2.60 | ||
| Dissipation factor | |||
| 50 Hz | 4.0E-4 | ||
| 60 Hz | 4.0E-4 | ||
| 1 MHz | 9.0E-4 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 70.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 35.0 | MPa | |
| fracture | 40.0 | MPa | |
| Tensile strain | |||
| yield | 5.0 | % | |
| fracture | 50 | % | |
| Bending modulus | 1500 | MPa | ISO 178 |
| bending strength | 55.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 240 to 260 | °C | |
| Barrel middle temperature | 260 to 280 | °C | |
| Barrel front temperature | 280 to 300 | °C | |
| Nozzle temperature | 260 to 280 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |