| About |
|---|
| 30% Glass Fiber Reinforced Flame Retardant, Halogen Free Polyamide 6.6 for Injection Moulding applications.&& |
| Product Description | |
|---|---|
| Supplier | Ram-On |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| Density | 1.40 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.30 to 0.70 | % | ISO 2577 |
| MD | 0.30 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.0 | % | ISO 62 |
| saturated | 6.0 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 1.9 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 1.9 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 110 | J/m | ASTM D256 |
| 23℃ | 10 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 225 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 225 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 238 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 238 | ℃ | ISO 75-2/B |
| Melting peak temperature | 256 | ℃ | ASTM D3417 |
| Melting temperature | 256 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric strength | 80 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 3.70 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 5VA | UL 94 | |
| Glowing wire flammability index | 850 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | 650 | ℃ | IEC 60695-2-13 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 150 | MPa | ASTM D638 |
| yield | 150 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 7600 | MPa | ASTM D790 |
| Bending modulus | 7600 | MPa | ISO 178 |
| bending strength | 200 | MPa | ASTM D790 |
| bending strength | 200 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| R-level | 120 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Barrel rear temperature | 270 to 280 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 285 to 310 | °C | |
| Mold temperature | 65 to 110 | °C | |
| Injection pressure | 70.0 to 125 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 35.0 to 85.0 | MPa | |
| Back pressure | 0.350 to 0.700 | MPa | |
| Screw speed | 60 to 90 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |