| POCAN® B1503 000000 PBT, non-reinforced, injection molding, extrusion&&POCAN® B1503 000000 PBT, non-reinforced, injection molding, extrusion&&POCAN® B1503 000000 PBT, non-reinforced, injection molding, extrusion&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ISO 1183 |
| Apparent density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：150℃，3. mm | 0.50 | % | |
| TD：260℃，3.0 mm | 1.9 | % | |
| MD：150℃，3.0 mm | 0.50 | % | |
| MD：260℃，3.0 mm | 1.9 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.50 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2470 | MPa | ASTM D638 |
| 23℃ | 2600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 55.0 | MPa | ISO 527-2/50 |
| Fracture, 23 ℃ | 33.8 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 23 ℃ | 8.0 | % | ISO 527-2/50 |
| Fracture, 23 ℃ | 29 | % | ASTM D638 |
| Nominal tensile fracture strain | |||
| 23℃ | > 20 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2090 | MPa | ASTM D790 |
| 23℃ | 2650 | MPa | ISO 178-A |
| bending strength | |||
| 23℃ | 85.5 | MPa | ASTM D790 |
| 23℃ | 90.0 | MPa | ISO 178-A |
| 3.50% strain, 23 ℃ | 80.0 | MPa | ISO 178-A |
| Bending strain | 6.0 | % | ISO 178/A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | < 10 | kJ/m² | |
| 23℃ | < 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 180 | kJ/m² | |
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -40℃ | < 10 | kJ/m² | |
| -30℃ | < 10 | kJ/m² | |
| 23℃ | < 10 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 150 | kJ/m² | |
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 60.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 180 | ℃ | ISO 306 |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 1.2E-4 | 1/℃ | |
| TD：23~55℃ | 1.2E-4 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| US FMVSS302 | passed | ISO 3795 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | ISO 7792-1-PBT, GHMR, 11-030 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – Dehumidifying desiccant | 120 | °C | |
| Drying time – Dehumidifying desiccant | 4.0 to 8.0 | hr | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 150x105x3mm, 1 hr |
| 3. 150x105x3mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |