| LLC6-008 is a Hexene copolymer certified resin designed for production of Blown films requiring a combination of good film stiffness and toughness. LLC6-008 contains no slip, medium antiblock and process aid. LLC6-008 complies with FDA regulation 21CFR 177.1520(c)3.2a and with most international regulations concerning the use of Polyethylene in contact with food articles. LLC6-008 is available in high antiblock, high slip and process aid. AVAILABLE FORMULATIONS B = Barefoot A = 0 Slip / High Anti Block F = Full Adds&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Food contact compliance,Low density,Copolymer,Hexene copolymers |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 25 µ m | 290 | MPa | ASTM D882 |
| 1% secant, TD: 25 µ m | 345 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, fracture, 25 µ m | 55.2 | MPa | ASTM D882 |
| TD, fracture, 25 µ m | 34.5 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 25 µ m | 400 | % | ASTM D882 |
| TD, fracture, 25 µ m | 700 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µm | 130 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：25 µm | 300 | g | ASTM D1922 |
| TD：25 µm | 650 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, 25.4 µ m, blow molded film | 65 | ASTM D2457 | |
| Haze | |||
| 25.4 µ m, blow molded film | 18 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |