| PolyOne’s Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| — | 0.30 | % | ISO 294-4 |
| — | 0.23 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 13000 | MPa | ISO 527-2 |
| — | 12500 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 210 | MPa | ISO 527-2 |
| fracture | 187 | MPa | ASTM D638 |
| Fracture, -40 ℃ | 217 | MPa | ISO 527-2 |
| Fracture, 100 ℃ | 123 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 , ASTM D638 |
| Fracture, -40 ℃ | 1.9 | % | ISO 527-2 |
| Fracture, 100 ℃ | 2.7 | % | ISO 527-2 |
| Bending modulus | |||
| — | 10500 | MPa | ISO 178 |
| — | 10900 | MPa | ASTM D790 |
| bending strength | |||
| — | 250 | MPa | ISO 178 |
| — | 296 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 70 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | 170 | J/m | ASTM D256 |
| Drop hammer impact | 8.13 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 252 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 254 | ℃ | ASTM D648 |
| 8.0 MPa, unannealed | 235 | ℃ | ISO 75-2/C |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 290 to 320 | °C | |
| Mold temperature | 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processing conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |