| About |
|---|
| P5200 is a pipe grade HDPE, produced by the Mitsui CX Technology. This resin is recommended for PE 63 compliant pressure pipes. P5200 combines excellent processability with good creep resistance, ESCR and mechanical properties.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,High ESCR |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 0.80 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 10% non-ionic detergent, molded, F50 | > 1000 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, molded | 180 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 67.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 121 | ℃ | ASTM D1525 3 |
| Oxygen sensing time | > 30 | min | ASTM D3895 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 65 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| Yield, molding | 25.0 | MPa | ASTM D638 |
| Fracture, molded | 38.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, molding | 7.0 | % | ASTM D638 |
| Fracture, molded | 650 | % | ASTM D638 |
| Bending modulus | |||
| Compression Molding | 1000 | MPa | ASTM D790-A |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 150 to 180 | °C | |
| Barrel 2 zone temperature | 150 to 180 | °C | |
| Barrel 3 zone temperature | 150 to 180 | °C | |
| Barrel 4 zone temperature | 150 to 180 | °C | |
| Barrel 5 zone temperature | 150 to 180 | °C | |
| Nozzle temperature | 170 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |