| About |
|---|
| LUVOCOM® 1200-7116是一种丙烯腈丁二烯苯乙烯(ABS)材料,含有的填充物为碳纤维增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 LUVOCOM® 1200-7116的主要特性为:传导性。&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Conductive |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 14 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，10 kg | 14.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.20 to 0.40 | % | DIN 16901 |
| Water absorption rate | |||
| 23℃，24hr | < 0.30 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 80.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 1.5 | % | ISO 527-2 |
| Bending modulus | 5000 | MPa | ISO 178 |
| bending strength | 105 | MPa | ISO 178 |
| Bending strain | 2.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 18 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 96.0 | ℃ | ISO 75-2/A |
| Continuous use temperature | 60.0 | ℃ | UL 746B |
| Maximum operating temperature | |||
| short-term | 80 | ℃ | |
| Vicat Softening Temp | 100 | ℃ | ISO 306/A |
| Linear coefficient of thermal expansion | |||
| MD | 4.0E-5 | 1/℃ | DIN 53752 |
| Thermal conductivity coefficient | 0.23 | W/m/K | DIN 52612 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+4 | ohms | IEC 60093 |
| insulation resistance | < 1.0E+4 | ohms | IEC 60167 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 70 to 95 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 220 to 250 | °C | |
| Barrel middle temperature | 220 to 250 | °C | |
| Barrel front temperature | 230 to 260 | °C | |
| Nozzle temperature | 220 to 250 | °C | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |