| About |
|---|
| Lustran® 308 resin is a low gloss, easy-flowing grade of ABS (acrylonitrile butadiene styrene). FEATURES Healthcare certifications Low gloss Easy flow balance of rigidilty, impact strength and abuse resistance APPLICATIONS Components of intravenous (IV)systems Surgical instruments Diagnostic test kits&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good liquidity,Low Gloss |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 220℃，10.0kg | 21 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 7.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 170 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 75.6 | ℃ | ASTM D648 |
| 0.45 MPa, annealed | 100 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 88.9 | ℃ | ASTM D648 |
| Vicat Softening Temp | 106 | ℃ | ASTM D1525 2 |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2210 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃ | 36.2 | MPa | ASTM D638 |
| Bending modulus | 2450 | MPa | ASTM D790 |
| bending strength | 72.4 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 218 to 260 | °C | |
| Mold temperature | 29 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |