| About |
|---|
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | 液态聚合物 |
| Material Status | Commercial: Negative |
| Features | V-0,Good Dimensional Stability |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.63 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD： | 0.03 | % | Internal Method |
| MD： | 0.39 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 250 | ℃ | ISO 75-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 MHz | 0.034 | kV/mm | IEC 60243-1 |
| 10 MHz | 0.007 | kV/mm | IEC 60243-1 |
| 1 KHz | 0.019 | kV/mm | IEC 60243-1 |
| Dissipation factor | |||
| 1 mm | 53 | MV/m | IEC 243-1 |
| 3 mm | 26 | MV/m | IEC 243-1 |
| Arc resistance | 151 | sec | |
| Compared to the leakage tracing index | 150 | V | IEC 60112 |
| Dielectric constant | |||
| 1 MHz | 3.7 | ||
| 1 KHz | 4.2 | ||
| 10 GHz | 3.6 | ||
| Surface resistivity | 1.0E+16 | ohm | IEC 60093 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 125 | MPa | ASTM D638 |
| tensile elongation | 2.8 | % | ASTM D638 |
| Bending modulus | 11000 | MPa | ISO 178 |
| bending strength | 160 | MPa | ISO 178 |
| Bending strain | 2.8 | % | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |