| Adsyl 7624 XCP is an advanced polyolefin, specially designed for use as a sealing layer in co-extruded and metallizable film applications. This grade features a very low seal initiation temperature and excellent optics. It provides enhanced processability on high speed BOPP lines. It contains anti-block additives. For regulatory information please refer to Adsyl 7624 XCP Product Stewardship Bulletin (PSB).&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Optical performance,High anti-blocking,Electroplating,Low temperature heat sealing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 6.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | ISO 527-3/25 | ||
| MD, 50 µ m, cast thin film | 260 | MPa | ISO 527-3/25 |
| TD, 50 µ m, cast thin film | 240 | MPa | ISO 527-3/25 |
| tensile strength | ISO 527-3/500 | ||
| MD, yield, 50 µ m, blow molded film | 15.0 | MPa | ISO 527-3/500 |
| TD, yield, 50 µ m, blow molded film | 14.0 | MPa | ISO 527-3/500 |
| tensile strength | ISO 527-3/500 | ||
| MD, fracture, 50 µ m, blow molded film | 41.0 | MPa | ISO 527-3/500 |
| TD, fracture, 50 µ m, blow molded film | 41.0 | MPa | ISO 527-3/500 |
| Tensile strain | ISO 527-3/500 | ||
| MD, fracture, 50 µ m, cast thin film | 900 | % | ISO 527-3/500 |
| TD, fracture, 50 µ m, cast thin film | 900 | % | ISO 527-3/500 |
| Tensile strain | ISO 527-3/500 | ||
| MD, yield, 50 µ m, cast thin film | 18 | % | ISO 527-3/500 |
| TD, yield, 50 µ m, cast thin film | 16 | % | ISO 527-3/500 |
| Initial sealing temperature | 105 | ℃ |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 61.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 107 | ℃ | ISO 306/A50 |
| Melting temperature | 132 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，50 µm | 87 | ASTM D2457 | |
| Haze | |||
| 50 µm | 1.2 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |