| High Impact , good chemical resistance sheet grade ABS designed for refrigerator liner applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Solvent resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 2.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.45 to 0.65 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2410 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 41.4 | MPa | |
| fracture | 35.9 | MPa | |
| Tensile strain | |||
| fracture | 55 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 2310 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 75.8 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 400 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 46.9 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 100 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 85.6 | ℃ | |
| Vicat Softening Temp | 113 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 87.8 to 93.3 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Recommended injection volume | 50 to 70 | % | |
| Barrel rear temperature | 193 to 210 | °C | |
| Barrel middle temperature | 210 to 227 | °C | |
| Barrel front temperature | 232 to 254 | °C | |
| Nozzle temperature | 232 to 274 | °C | |
| Processing (melt) temperature | 232 to 274 | °C | |
| Mold temperature | 48.9 to 82.2 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |