| About |
|---|
| Polypropylene homopolymer with high melt flow rate for injection applications. ISPLEN® PP 080 A shows a high stiffness and a low warpage shrinkage behaviour. This product is standard stabilised and also antistatic formulated. APPLICATIONS Small domestic containers. Rigid packages. Small boxes for cosmetic. Gardens furniture.&& |
| Product Description | |
|---|---|
| Supplier | REPSOL |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,High liquidity,Low contractility,Antistatic property |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ISO 1133 |
| Shrinkage rate | 1.2 | % | ISO 2577 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40℃ | 1.5 | kJ/m² | ISO 179 |
| -20℃ | 1.6 | kJ/m² | ISO 179 |
| 0℃ | 1.6 | kJ/m² | ISO 179 |
| 23℃ | 2.5 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -40℃ | 14 | kJ/m² | ISO 179 |
| -20℃ | 14 | kJ/m² | ISO 179 |
| 0℃ | 18 | kJ/m² | ISO 179 |
| 23℃ | 81 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ISO 180 | ||
| 0℃ | 2.5 | kJ/m² | ISO 180 |
| 23℃ | 2.6 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | ISO 180 | ||
| 0℃ | 20 | kJ/m² | ISO 180 |
| 23℃ | 60 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 81.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 71.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 152 | ℃ | ISO 306/A120 |
| B120 | 56.0 | ℃ | ISO 306/B120 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 68 | ISO 868 | |
| Tensile modulus | 1300 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 28.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 14 | % | ISO 527-2 |
| Bending modulus | 1300 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 150x100x3mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |