| About |
|---|
| Zythane 5080A is a polyester--based TPU specifically formulated for extrusion applications. It exhibits excellent abrasion resistance and toughness and has good hydrolytic stability, oil, fuel and solvent resistance. It is supplied uncolored in pellet form. Typical Applications: Zythane 5080A applications include among others spiral and pneumatic tubing, round and V belting, blow molded bellows.&& |
| Product Description | |
|---|---|
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Hydrolysis stability,Good wear resistance,Grease resistance,Solvent resistance,Fuel resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 80 | ASTM D2240 | |
| Taber abraser | 24.0 | mg | ASTM D1044 |
| Abrasion（DIN） | 25 | mm³ | DIN 53516 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 33.0 | MPa | ASTM D412 |
| 300% strain | 103 | MPa | ASTM D412 |
| 100% strain | 4.00 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 680 | % | ASTM D412 |
| tear strength | 73.6 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 24℃，22 hr | 0.18 | % | ASTM D395B |
| 70℃，72 hr | 0.32 | % | ASTM D395B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -37.2 | ℃ | DSC |
| Vicat Softening Temp | 82.2 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 85 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 175 | °C | |
| Barrel middle temperature | 190 | °C | |
| Barrel front temperature | 205 | °C | |
| Nozzle temperature | 205 to 210 | °C | |
| Processing (melt) temperature | 200 to 205 | °C | |
| Mold temperature | 25 to 60 | °C | |
| Back pressure | 0.500 to 1.00 | MPa | |
| Screw speed | 60 to 200 | rpm | |
| Clamping force | 4.1 to 6.9 | kN/cm² | |
| Drying temperature | 85 | °C | |
| Drying time | 4.0 | hr | |
| Barrel 1 zone temperature | 175 | °C | |
| Barrel 2 zone temperature | 190 | °C | |
| Barrel 3 zone temperature | 205 | °C | |
| Nozzle temperature | 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |