Clariant PBT PBT-1100G30

About
Clariant PBT PBT-1100G30 is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber. It is available in North America for injection molding. Important attributes of Clariant PBT PBT-1100G30 are: Flame Rated Chemical Resistant Good Dimensional Stability Good Toughness Heat Resistant Typical applications include: Engineering/Industrial Parts Housings Wire & Cable&&

Product Description
Supplier	Clariant
Generic	polybutylene terephthalate
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Solvent resistance,HB
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.53	g/cm³	ASTM D792
Shrinkage rate
MD：3.2 mm	0.50	%	ASTM D955
Water absorption rate
24hr	0.060	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
3.2mm	64	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	207	℃	ASTM D648
0.45 MPa, unannealed	221	℃	ASTM D648
Melting temperature	220 to 225	℃
Linear coefficient of thermal expansion
MD	2.7E-5	1/℃	ASTM D696
Relative temperature index
Electrical performance, 0.80 mm	75.0	℃	UL 746
Strength mechanical performance, 0.80 mm	75.0	℃	UL 746
Impact mechanical performance, 0.80 mm	75.0	℃	UL 746

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1.0E+16	ohms·cm	ASTM D257
Dielectric strength	17	kV/mm	ASTM D149
Arc resistance
3.18 mm	150	sec	ASTM D495
Compared to the resistance to leakage and marking index
3.18 mm	325	V	UL 746
High Arc Burning Index (HAI) (0.820 mm)	120		UL 746
High voltage arc marking rate (HVTR) (3.17 mm)	52.5	mm/min	UL 746
Hot wire ignition
HWI			UL 746
0.820 mm	23	sec	UL 746
1.58 mm	90	sec	UL 746
3.18 mm	120	sec	UL 746

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level		UL 94
0.80 mm	HB	UL 94
1.60 mm	HB	UL 94
3.20 mm	HB	UL 94
6.40 mm	HB	UL 94

MECHANICAL	Nominal value	Unit	Test method
tensile strength	107	MPa	ASTM D638
Tensile strain
fracture	3.0	%	ASTM D638
Bending modulus	7580	MPa	ASTM D790
bending strength	183	MPa	ASTM D790
Rockwell hardness			ASTM D785
M-level	84		ASTM D785
R-level	119		ASTM D785

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	121	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.020	%
Barrel rear temperature	232 to 274	°C
Barrel middle temperature	232 to 274	°C
Barrel front temperature	232 to 274	°C
Processing (melt) temperature	232 to 246	°C
Melt temperature (target)	241	°C
Mold temperature	66 to 82	°C
Injection speed	Fast
Back pressure	0.345 to 0.689	MPa
Screw speed	20 to 80	rpm
Cushion	3.18 to 6.35	mm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.