| Characteristics: Excellent Dart Impact,Excellent Processability, Excellent Sealability Comonomer: hexcene-1 Additives: Antioxidant ,Polymer Processing Aid&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good heat sealing,High impact resistance,Inoxidizability,Hexene copolymers |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| tensile strength | |||
| Fracture, molded | 39.2 | MPa | ASTM D638 |
| MD, fracture, 50 µ m | 53.9 | MPa | |
| TD, fracture, 50 µ m | 49.0 | MPa | |
| Tensile strain | |||
| Fracture, molded | 800 | % | ASTM D638 |
| MD, fracture, 50 µ m | 600 | % | |
| TD, fracture, 50 µ m | 650 | % | |
| Drop hammer impact | |||
| 50 µm | > 1000 | g | ASTM D1709 |
| tear strength | |||
| MD，50 µm | 117.7 | kN/m | ASTM D1922 |
| TD，50 µm | 166.7 | kN/m | ASTM D1525 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 117 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 50 µm | 15 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 140 | °C | |
| Barrel 2 zone temperature | 160 | °C | |
| Barrel 3 zone temperature | 170 | °C | |
| Connector temperature | 170 | °C | |
| Nozzle temperature | 170 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |