| PA 66 chemically reinforced with 10 % glass fibre and with the content of 20% glass beads. Improved anisotropy of shrinkage. The relation of the anisotropy to the mechanical properties can be changed by the ideal combination of the glass fibre and the glass beads. High surface brightness, low rolling resistance force. Manufacturing of exact parts /mainly in flat form/, throttle valves in air piping. Increased strength and tension modulus in tension due to the addition of glass fibre. Delivered in the full RAL colour scale.&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,Chemical coupling,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 275℃，0.325kg | 1.0 | g/10min | ISO 1133 |
| Shrinkage rate | STM 64 0808 | ||
| TD | 1.6 | % | STM 64 0808 |
| MD | 1.0 | % | STM 64 0808 |
| water content | 0.15 | % | ISO 960 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5000 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 90.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 2.0 | % | ISO 527-2 |
| Bending modulus | 5400 | MPa | ISO 178 |
| bending strength | 140 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20℃ | 3.0 | kJ/m² | ISO 179 |
| 23℃ | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -20℃ | 14 | kJ/m² | ISO 179 |
| 23℃ | 20 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 250 | ℃ | ISO 306/B |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric strength | 40 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 450 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 | |
| Igniting temperature of the hot wire | 650 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 70 to 80 | °C | |
| Injection pressure | 70.0 to 120 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |