SLOVAMID® 6 GB 20

About
Nearly ideal anisotropy of shrinkage in the vertical and in the horizontal direction is established. Manufacturing of exact mouldings. Disadvantage are the relatively low mechanical properties, these can be modified by addition of GF, as a result of which the anisotropy worsens.PA 6 for injection moulding, reinforced with 20% glass beads offers high grade surface brightness, low rolling resistance force. Application: eg. throttle valves for air piping. Delivered in natural mode and in the full RAL colour scale.&&

About

Nearly ideal anisotropy of shrinkage in the vertical and in the horizontal direction is established. Manufacturing of exact mouldings. Disadvantage are the relatively low mechanical properties, these can be modified by addition of GF, as a result of which the anisotropy worsens.PA 6 for injection moulding, reinforced with 20% glass beads offers high grade surface brightness, low rolling resistance force. Application: eg. throttle valves for air piping. Delivered in natural mode and in the full RAL colour scale.&&

Product Description
Generic	PA6
Material Status	Commercial: Active
Features	Good surface appearance,Good Dimensional Stability,HB
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.24	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	3.0	g/10min	ISO 1133
Shrinkage rate			STM 64 0808
TD	1.6	%	STM 64 0808
MD	1.5	%	STM 64 0808
water content	0.15	%	ISO 960

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3300	MPa	ISO 527-2
tensile strength
yield	45.0	MPa	ISO 527-2
Tensile strain
yield	20	%	ISO 527-2
Bending modulus	2800	MPa	ISO 178
bending strength	85.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-20℃	1.5	kJ/m²	ISO 179
23℃	2.5	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-20℃	45	kJ/m²	ISO 179
23℃	45	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	50.0	℃	ISO 75-2/B
Vicat Softening Temp	200	℃	ISO 306/B
Melting temperature
DSC	220	℃	ISO 3146

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94
Igniting temperature of the hot wire	650	℃	IEC 60695-2-13

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Processing (melt) temperature	250 to 270	°C
Mold temperature	50 to 70	°C
Injection pressure	70.0 to 100	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.