| Flexible, non-halogenated FR, PPE+Polyolefin resin designed for evaluation in Automotive ISO6722 Class A-C applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+Polyolefin |
| Material Status | Commercial: Active |
| Features | Good flexibility,Halogen free,Flame Characteristics |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 20 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 20.9 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 30 seconds | 65 | ASTM D2240 | |
| Tensile modulus | 1450 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 37.0 | MPa | ISO 527-2/50 |
| fracture | 37.0 | MPa | ASTM D638 |
| yield | 37.0 | MPa | ASTM D638 |
| yield | 39.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 38 | % | ISO 527-2/50 |
| fracture | 45 | % | ASTM D638 |
| yield | 17 | % | ISO 527-2/50 |
| yield | 37 | % | ASTM D638 |
| Bending modulus | 1260 | MPa | ISO 178 |
| 50 mm span | 1150 | MPa | ASTM D790 |
| bending strength | 44.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 41.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 43 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 550 | J/m | ASTM D256 |
| -30℃ | 9.0 | kJ/m² | ISO 180-1A |
| 23℃ | 41 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 42.0 | J | ASTM D3763 |
| 23℃，Total Energy | 33.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 93.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 84.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 115 | ℃ | ASTM D648 |
| Vicat Softening Temp | 71.0 | ℃ | ASTM D1525 9 |
| Vicat Softening Temp | |||
| B50 | 71.0 | ℃ | ISO 306 |
| B120 | 76.0 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 1.3E-4 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 8.2E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 1 MHz | 2.55 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 2.0E-3 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 to 80 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 210 to 260 | °C | |
| Barrel 3 zone temperature | 230 to 285 | °C | |
| Barrel 5 zone temperature | 250 to 285 | °C | |
| Melt temperature | 250 to 285 | °C | |
| Nozzle temperature | 250 to 285 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |