| Eraclene BB 82 is a high density polyethylene resin (HDPE), with antioxidants, suitable for blow moulding application. It is especially recommended for the production of containers up to 220 liters. Main Application Eraclene BB 82 provides an excellent combination of extrudability and parison stability, which, in turn, allows to obtain an uniform wall thickness in large blow moulded parts. Eraclene BB 82 is ideal for the production of various industrial containers. Its broad molecular weight distribution leads to an outstanding environmental stress cracking resistance (ESCR) in combination with a good rigidity.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Inoxidizability,Wide molecular weight distribution,Food contact compliance,High ESCR,High density |
| Availabilitys | North America,Latin America,Asia Pacific,Europe,Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.954 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 0.15 | g/10min | ISO 1133 |
| 190℃，21.6kg | 5 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Compression Molding | > 750 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| Compression Molding | 无断裂 | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Brittleness temperature | < -60.0 | ℃ | ASTM D746 |
| Vicat softening point | 127 | ℃ | ISO 306/A |
| Melting point | 132 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hardness Shore | |||
| Shaw’s D, molded | 65 | ISO 868 | |
| Yield yld, molded | 27.0 | MPa | ISO 527-2 |
| Broken BRK, molded | 30.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Broken BRK, molded | > 600 | % | ISO 527-2 |
| Flexural modulus | |||
| Compression Molding | 1200 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Forming conditions | Nominal value | Unit | Test method |
| Barrel 1 Temperature Zone 1 Temperature | 180-190 | ℃ | |
| Barrel 2 Temperature Zone 2 Temperature | 195-205 | ℃ | |
| Barrel 3 Temperature Zone 3 Temperature | 195-205 | ℃ | |
| Barrel 4 Temperature Zone 4 Temperature | 195-205 | ℃ | |
| Head Temperature | 195-205 | ℃ | |
| Mold Temperature | 195-205 | ℃ | |
| Operation temperature | 205-215 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |